http://dspace.bsuedu.ru/handle/123456789/63388| Название: | Microstructural evolution of a re-containing 10% Cr-3Co-3W steel during creep at elevated temperature |
| Авторы: | Fedoseeva, A. Brazhnikov, I. Degtyareva, S. Nikitin, I. Kaibyshev, R. |
| Ключевые слова: | technique metal science high-chromium steels creep microstructural evolution softening strengthening mechanism Zener pressure |
| Дата публикации: | 2023 |
| Библиографическое описание: | Microstructural evolution of a re-containing 10% Cr-3Co-3W steel during creep at elevated temperature / A. Fedoseeva, I. Brazhnikov, S. Degtyareva [et al.] // Metals. - 2023. - Vol.13, №10.-Art. 1683. |
| Краткий осмотр (реферат): | The microstructural evolution of a Re-containing 10% Cr-3Co-3W steel with low N and high B content during creep was investigated at different strains at 923 K and under an applied stress of 120 MPa using TEM and EBSD analyses. The studied steel had been previously normalized at 1323 K and tempered at 1043 K for 3 h |
| URI (Унифицированный идентификатор ресурса): | http://dspace.bsu.edu.ru/handle/123456789/63388 |
| Располагается в коллекциях: | Статьи из периодических изданий и сборников (на иностранных языках) = Articles from periodicals and collections (in foreign languages) |
| Файл | Описание | Размер | Формат | |
|---|---|---|---|---|
| Fedoseeva_Microstructural_23.pdf | 2.65 MB | Adobe PDF | Просмотреть/Открыть |
Все ресурсы в архиве электронных ресурсов защищены авторским правом, все права сохранены.